John Joseph Howe

Supersaturated hcp f -Zr alloys containing 22-28 at.% N were prepared by nitriding sheets of Zr in an atmosphere of high-purity N 2 , followed by homogenization under high-purity Ar gas. Quenching and isothermal ageing of the alloys for various times between 500 and 650°C resulted in precipitation of a metastable phase, rather than the equilibrium phase ZrN. This investigation focused on determining the structure, orientation relationship, habit plane, morphology, growth kinetics and atomic growth mechanism of this non-equilibrium precipitate using transmission electron microscopy imaging and diffraction techniques, high-resolution transmission electron microscopy, electron-energy-loss spectroscopy and various simulation programs. The precipitate, which was arbitrarily designated the  phase, has a monoclinic Bravais lattice. Its lattice parameters are a = 0.32 nm, b = 0.60 nm, c = 0.56 nm, f = g = 90° and n = 121.5°. Its orientation relationship with the f matrix is $$ _alpha /mskip-2/ _xiquad adquad [01bar 10] _alpha /mskip-2/ [001]_xi, $$ and the average habit plane of lenticularly shaped precipitates is $_alpha$ . Determination of the structure and other aspects of the phase transformation are discussed