We have observed the formation of extended defects in silicon at low temperatures by means of in-situ high-resolution transmission electron microscopy . The defects are distorted spheres, occasionally truncated by facets, less than 5 nm in diameter. These defects are stable up to 773 K, and they gradually shrink during annealing in the temperature range from 773 to 973 K. From the analysis of HRTEM images of the defects, we have suggested that the defects are voids formed via athermal migration …
Read moreWe have observed the formation of extended defects in silicon at low temperatures by means of in-situ high-resolution transmission electron microscopy . The defects are distorted spheres, occasionally truncated by facets, less than 5 nm in diameter. These defects are stable up to 773 K, and they gradually shrink during annealing in the temperature range from 773 to 973 K. From the analysis of HRTEM images of the defects, we have suggested that the defects are voids formed via athermal migration of vacancies under electron irradiation