Abstract: Samples of LaxSr1-xMnO3 (x = 0.5, 0.55, 0.6, 0.66, and 0.7) were prepared by the citrate-nitrate autocombustion method. The prepared nano-particles were investigated and characterized using X-Ray diffraction (XRD) and Transmission Electron Microscopy (TEM) to confirm the formation of the samples in single phase without any impurities and to calculate the particle size. The magnetic susceptibility χM was measured as a function of temperature and magnetic field intensity. From χM(T) and …
Read moreAbstract: Samples of LaxSr1-xMnO3 (x = 0.5, 0.55, 0.6, 0.66, and 0.7) were prepared by the citrate-nitrate autocombustion method. The prepared nano-particles were investigated and characterized using X-Ray diffraction (XRD) and Transmission Electron Microscopy (TEM) to confirm the formation of the samples in single phase without any impurities and to calculate the particle size. The magnetic susceptibility χM was measured as a function of temperature and magnetic field intensity. From χM(T) and M(H) the saturation magnetization (Ms), remanent magnetization (Mr) and coercivity (Hc) of the samples were estimated. The correlation among physical properties and the ratio of divalent cation substitution was discussed and reported to shed more light on technological applications of the investigated samples.